|Product Name:||Heavy Tungsten Alloy Bar||Type:||WNiFe/WNiCu|
|Density:||16.4-18.5 G/cc||Purity:||>90% W|
|Tensile Strength:||700-1400 MPa||Elongation:||<9%|
|Standard:||ASTM B777-2009||Applications:||Armor-piercing Ammunition|
WNiFe Heavy Tungsten Alloy Bar,
WNiCu Heavy Tungsten Alloy Bar,
Tungsten Alloy Bar ASTM B777
Heavy Tungsten Alloy Bar is based on tungsten (tungsten content is generally 80% ~ 98%), adding a small amount of nickel, iron, copper, cobalt, molybdenum, chromium and other elements of the alloy material. The density of high specific gravity tungsten alloy is up to 15.20~18.70g/cm3, also known as high specific gravity tungsten alloy or high density alloy material. Because tungsten alloys weigh more than twice as much as steel.
|32 Max||30 Max||40 Min||33 Max||31 Max||40 Min||34 Max||32 Max||35 Max||33 Max|
|Tensile Strength (Max)||770 Min||900 Min||1400
|770 Min||910 Min||1440 Max||735 Min||920 Min||700 Min||850 Min|
|620 Min||620 Min||1280 Max||650 Min||650 Min||1340 Max||650 Min||650 Min||-||-|
|5 Min||15 Min||5 Min||5 Min||12 Min||3 Min||3 Min||12 Min||2 Min||6 Min|
Heavy tungsten alloy is mainly divided into two series: W-Ni-Fe and W-Ni-Cu, and even W-Ni-Fe-Cu. In contrast, W-Ni-Fe alloy has good mechanical properties and plays an important role in various fields of national defense industry and national economy. It is a very important new military material in national defense industry and has been gradually promoted to various civil industries.
The tungsten content in tungsten alloys varies between 90% and 98%, which is responsible for their high density (16.5 to 19.00 g/cc). Nickel, iron and/or copper are used as metal adhesive substrates to hold brittle tungsten particles together, making the tungsten alloy ductile and easy to work. Ferric nickel-nickel is the most commonly used additive with a ratio of 7Ni:3Fe or 8Ni:2Fe (by weight).
The United States has developed a 97W-2.1Ni-0.9Fe alloy with an 80-gram warhead that can penetrate an inch thick military steel plate at a limit speed of 3,580 ft/s.