WNiCu Machined Tungsten Alloy Shafts High Performance 95% W For Motor Engine
|Place of Origin:||CHINA|
|Model Number:||WNiFe - Tungsten Heavy Alloy Bolts|
Payment & Shipping Terms:
|Minimum Order Quantity:||10 kg|
|Packaging Details:||plywood cases|
|Delivery Time:||15-20 days|
|Payment Terms:||L/C, T/T, D/P, Western Union|
|Supply Ability:||2000 kg per month|
|Product Name:||Tungsten Heavy Alloy Bolts||Type:||WNiFe|
|Tensile Strength:||750-1400 MPa||Elongation:||<10%|
Tungsten Heavy Alloy Bolts,
90%WNiFe Tungsten Heavy Alloy Bolts,
Tungsten Alloy Bolts High Temperature Resistance
Tungsten Heavy Alloy Bolts are made of tungsten base (tungsten content is generally 80%~98%) and a small amount of nickel, iron, copper, cobalt, molybdenum, chromium and other elements. The density of gravity tungsten alloy is as high as 15.20~18.70g/cm3, also known as gravity tungsten alloy or high-density alloy material. Because tungsten alloy weighs more than twice as much as steel.
|32 Max||30 Max||40 Min||33 Max||31 Max||40 Min||34 Max||32 Max||35 Max||33 Max|
|Tensile Strength (Max)||770 Min||900 Min||1400
|770 Min||910 Min||1440 Max||735 Min||920 Min||700 Min||850 Min|
|620 Min||620 Min||1280 Max||650 Min||650 Min||1340 Max||650 Min||650 Min||-||-|
|5 Min||15 Min||5 Min||5 Min||12 Min||3 Min||3 Min||12 Min||2 Min||6 Min|
Tungsten alloy has a series of excellent properties, high specific gravity: general gravity lead 16.5-18.75g/cm3, high strength: tensile strength 700-1000mpa, strong light absorption capacity: 30-40% higher than general gravity lead, and thermal conductivity: 5 times of modulus steel; Low thermal expansion coefficient: only 1 / 2-1 / 3 of carbon steel, good conductivity and good welding processing skills.
A common method of making heavy tungsten alloys is to mix the desired amount of tungsten, iron, nickel or copper powder, then cold-press and liquid-phase sinter to near full density. During the liquid phase treatment, the matrix tungsten alloy is melted, and part of the tungsten enters the solution to form a microstructure, so that larger tungsten particles (20-60m) are dispersed in the matrix alloy.